INS 110
A plastically moulded insulating brick rated to 1100 °C service, at 0.98 g/cc bulk density and 62% apparent porosity, with thermal conductivity of 0.28 kcal/m/hr/°C at 500 °C hot face. Cold crushing strength is 32 kg/cm² — enough to build with, not enough to carry a load.
| NATURE OF BOND | CERAMIC |
|---|---|
| SHAPING | PLASTICALLY MOULDED |
| MAX.SERVICE TEMPERATURE | 1100°C |
| Reversible Thermal Expansion | 0.50% at 1000°C |
| Al₂O₃ content, % | 23.2 |
| Fe₂O₃ content, % | 2.07 |
| Bulk density g/cc | 0.98 |
| Apparent Porosity % | 62 |
| Cold crushing strength kg/cm2 | 32 |
| Refractoriness Orton /°C | 18 / +1522 |
| PLC % after heating at 1400°C / 5 hrs | -0.3 |
| Thermal Conductivity Kcal/m/hr/°C at 500°C HF | 0.28 |
Values as published by the manufacturer. Manufacturer TDS governs.
More in Bricks
Bricks
INS 140
Bricks
High Alumina Fire Brick — 30%
Bricks
High Alumina Fire Brick — 40%
Bricks
High Alumina Fire Brick — 50%
Bricks
High Alumina Fire Brick — 60%
Bricks
High Alumina Fire Brick — 70%
Bricks
High Alumina Fire Brick — 80%
Bricks
Acid Resistant Brick
Bricks
Magnesite Brick — 90%
Bricks
Magnesite Brick — 91%
Bricks
HFK Insulation Brick
Bricks
Porosint 500
Bricks
Porosint 750
Bricks
Alumina Burner Block
Bricks
Refractory Fire Tile