WHYTHEAT K SUPREME

68–72% alumina rated to 1700 °C, at 9.5–10.5% water and 2.40 g/cc dried, reaching 450 kg/cm² after drying and 480 kg/cm² after firing at 1550 °C. Iron oxide is 0.9% and lime 3.8%, both lower than the standard Whytheat K.

WHYTHEAT K SUPREME — product visual
Representative product visual
Technical specifications for WHYTHEAT K SUPREME
NATURE OF BONDHYDRAULIC
INSTALLATIONVIBRATION CASTING
MAX.SERVICE TEMPERATURE1700°C
MAXIMUM GRAIN SIZE5 mm
WATER REQUIRED FOR CASTING9.5 - 10.5%
Al₂O₃ content, %68 - 72
CaO3.8
Fe₂O₃ content, %0.9
Dry density g/cc After drying at 110°C/ 24hrs2.40
CCS kg/cm2 After drying at 110°C/ 24hrs450
After heating at 1100°C/ 3hrs280
After heating at 1550°C/ 3hrs480
% Retained on maximum size0.5
Refractoriness, Orton /°C33/1705
After heating at 1100°C/ 3hrs-0.10
After heating at 1500°C/ 3hrs-1.5
PACKING25KG BAG

Values as published by the manufacturer. Manufacturer TDS governs.